2. TD S - WP - MS02 - 000_01/21 CHARACTERISTICS TEST METHOD UNIT NOMINAL VALUES Length m 10.00 Width m 1.00 Nominal Thickness UEAtc mm 4.0 Reinforcement base UEAtc gms/ m 2 20 0 Straightness m 20 mm х 10 m Bitumen Softening Point ASTM D - 36 ̊ C 125 Tensile Strength, Longitudinal Transversal DIN EN 12311 - 11 DIN EN 12311 - 11 N/5cm N/5cm 950 70 0 Elongation at Break, Longitudinal Transversal DIN EN 12311 - 11 DIN EN 12311 - 11 % % 5 0 5 5 Tear Resistance, Longitudinal Transversal ASTM D5147 ASTM D5147 N 5 50 40 0 Lap Joint Strength, Longitudinal Transversal DIN 52123 DIN 52123 N/5cm N/5cm > 900 > 7 0 0 Cold Flexibility @ low temperature DIN 52123 - 5 to - 1 0 ̊C No Cracking Heat Resistance @ 135 ̊C DIN 52123 ̊C ( No Flowing ) Water Absorption ( BSP ) ASTM D5147 % <0.2 Resistance to Thermal Ageing. UEAtc No Deterioration Hydrostatic Pressure Resistance @5 Bar BS EN 12390 - No Leakage All values are subject to 5 - 10 % tolerance TECHNICAL CH ARACTERISTICS NOTE: The information contained in this DATA SHEET, as well as our advice, both written as oral or provided through testing, are based on our experience, and they do not constitute any product guarantee for the installer, who must take them as simple orientations, provided strictly as information. We recommend to study deeply all information provided before proceeding to the use or application of any of our products, and strongly advise to conduct tests “on - site” in order to determi ne their convenience for a specific project. Our recommendations do not exempt of the obligation that installers have to deeply know the right application method for these systems before they use them, as well as to conduct as many preliminary tests as pos sible if there are any doubts about the appropriate system to use. The application, use and processing of our products are beyond our control, and therefore under the exclusive responsibility of the installer. In consequence, the installer will be the only responsible of any damage or prejudice derived from the partial or total in - observation of our indications, and in general, of the inappropriate use or application of these materials. Sajaa Industrial Area behind Sharjah Cement Factory, Sharjah U.A.E. Email: info@royalwayindustries.com PO BOX: 65034 Tel: +971 6 572 6378 Website: www.royalwayindustries.com ROYAL WAY INDUSTRIES LLC Page 2

1. TD S - WP - MS02 - 000_01/21 PROPRETIES C H AR A C TERISTICS Polymer (SBS) modified bituminous membrane, reinforced with non - woven polyester mat. The Polyester combines high tensile strength with an elongation above 50%. A high performance elastomeric waterproofing membrane which combines that ability to withstand high ambient temperature with the usual characteristics of an SBS membrane of high flexibility at low temperature t hat mak es it easy to apply at sub - zero temperature. NEOFLEX S4 20 0 SBS Modified Bituminous Membrane Page 1  Cold flexibility  Heat stability  Thermal ageing resistance  UV resistance  Resistance to foot traffic ADVANTAGES  Positive vapour barrier  Excellent resistance to atmospheric agents.  High flexib ility during application at sub - zero temperature with no physical strains  High malleability making it entirely suitable for difficult basement and foundation works.  High softening point allowing it to maintain shape stability at high temperatures.  Withstan ds thermal shocks.  Accommodates structural movements.  Resistant to chemical attacks. SPECIAL FEATURES It is covered either with polyethylene film or sand at the back and comes in a variety of surface finishes; sand, polyethylene film, slated or aluminium. The slate can be natural grey, white, black or green or any other colour depending on stock availability. SURFACE FINISH It is produced 4mm thick in rolls of 1 × 10 meters. The rolls are palletized and shrink wrapped. T HICKNESS , R OLL S IZE & P ACKING The rolls should always be stor ed vertically in a shaded area. Normally the pallets sho uld not be stacked one over the other. However, if a woode d board is used in between, two pallets may be stacked one over the other. STORAGE & MATERIAL HANDLING PREPARATION Where the membrane is to be laid directly on to a one - layer system on concrete, tiles or a n existing roofing system, a coat of bituminous pri mer should first be applied and allowed to dry thoroughly. APPLICATION INSTRUCTIONS The membrane must be unroll ed and laid down on the area to which it is to be applied. Check the orientation carefully. Adjacent rolls should the n be laid, each overlapping the one next to it by 10cms on t he side and 15 cms at the ends. Taking care not to chan ge to orientation of each roll, reverse the process unti l each has been re - rolled. When laying the roll, the lower surface should be heate d with a propane torch, using sw eeping left to right movements. This will melt the lower surfa ce to the membrane and allow it to stick to the sub strate. On slated membranes you should either remove the sp ecial selvedge paper or on sand bottom rolls torch the special polypropylene selvedge. Continue this pr ocess for each subsequent roll, remembering that the overlaps must be 10cms for the edges and 15cms a t the ends. When the process is complete, carry out an inspection to ensure total adhesion. Used in one or two layers to roofs, foundations works, basement tanking, where hi gh flexibility and malleability are required. FUNCTIONS