2. TDS - WP - MG01 - 000_01/21 Tests Performed – As per ASTM Procedure Units Tolerance Value Length m < - 1% 10.00 Width m < - 1% 1.00 Thickness UEAtc mm - 0.2mm 4.0 Tensile Strength, Longitudinal Transversal ASTM D5147 ASTM D5147 N/50mm N/50mm - 20% - 20% 75 0 55 0 Elongation at Break, Longitudinal Transversal ASTM D5147 ASTM D5147 % % - 15 - 15 40 45 Tear Resistance, Longitudinal Transversal ASTM D5147 ASTM D5147 N N min min 5 50 375 Lap Joint Strength, Longitudinal Transversal ASTM D5147 ASTM D5147 N/5cm N/5cm - 20% - 20% 750 550 Flexibility at Low Temperature * ASTM D5147 C min 0 Dimensional Stability at 80C Longitudinal Transversal ASTM D5147 ASTM D5147 % % mlv mlv - 0.5 - 0.5 Water Absorption (n/a slate) ASTM D5147 % mlv <0.15 Root Resistance Contains 1% Preventol B2 DIN 4062 - - Conforms All values are subject to 5 - 10 % tolerance TECHNICAL CH ARACTERISTICS NOTE: The information contained in this DATA SHEET, as well as our advice, both written as oral or provided through testing, are based on our experience, and they do not constitute any product guarantee for the installer, who must take them as simple orientations, provided strictly as informatio n. We recommend to study deeply all information provided before proceeding to the use or application of any of our products, and strongly advise to conduct tests “on - site” in order to determine their convenience for a specific project. Our recommendations do not exempt of the obligation that installers have to deeply know the right application method for these systems before they use them, as well as to conduct as many preliminary tests as possible if there are any doubts about the appropriate system to use . The application, use and processing of our products are beyond our control, and therefore under the exclusive responsibility of the installer. In consequence, the installer will be the only responsible of any damage or prejudice derived from the partial or total in - observation of our indications, and in general, of the inappropriate use or application of these materials. Sajaa Industrial Area behind Sharjah Cement Factory, Sharjah U.A.E. Email: info@royalwayindustries.com PO BOX: 65034 Tel: +971 6 572 6378 Website: www.royalwayindustries.com R OYAL WAY INDUSTRIES LLC Page 2

1. TDS - WP - MG01 - 000_01/21 PROPRETIES C H AR A C TERISTICS A high performance elastomeric waterproofing membrane which combines the ability to withstand high ambient temperature with the usual characteristics of an SBS membrane of high flexibility at low temperature that makes it easy to apply at sub - zero temperature. The SBS Bitumen Compound is carefully blended with high quality anti - root additives that makes it suitable for all typ es of waterproofing works especially roofs gardens, flower Boxes and underground backfilled structures. NEOFLEX S4180 - G SBS Modified Bituminous Membrane Page 1  Cold flexibility  Heat stability  Thermal ageing resistance  UV resistance  Resistance to foot traffic ADVANTAGES  Positive vapour barrier  Excellent resistance to atmospheric agents.  High flexibility during application at sub - zero temperature with no physical strains  High malleability making it entirely suitable for difficult basement and foundation works.  High softening point allowing it to maintain shape stability at high temperatures.  Withstands thermal shocks.  Accommodates structural movements.  Resistant to chemical attacks. SPECIAL FEATURES The surface finish is sanded plain. SURFACE FINISH It is available in 1 m wide and 10 m length. T HICKNESS , R OLL S IZE & P ACKING NEOFLEX G waterproofing membranes is reinforced with 180 g/m² non - woven spu n bond polyester reinforcement t hat gives the mem brane dimensional stability and resistance to puncture . It is coated with a specially formulated mixture of SB S modified bitumen and antiriot additive which makes the membrane resistant to water, atmospheric agents, and plantations roots an d malleable at low tem perature while retaining a high softening point. REINFORCEMENT CORE AND COATING MIXTURE APPLICATION INSTRUCTIONS The membrane must first be unrolled and laid down on the area to which it is to be applied. Check the orientation carefully. Adjacent rolls should then be laid, each overlapping the one next to it by 10 cm on the side and 15 cm at the ends . Taking care not to change the orientation of each roll, rev erse the process until each has been r e - rolled. When lay ing the roll, the lower surface should be heated with a propane torch, using sweeping left to right movements. T his will melt the lower surface of the membrane and allo w it to stick to the substrate. Continue this pr ocess for each subsequent roll, remembering that the overlaps must be 10 cm for the edges and 15 cm at the ends. When the proc ess is complete, carry out an inspe ction to ensure total adhesion. When applied in a total ly bonded system, a coat of NEO prime WB or NEO prime S B should be applied at the rate of 200 - 300 g/m2.