2. TDS - WP - N T01 - 000_ 01/20 PROPERTIES TYPICAL VALUES TEST STANDARDS Color White/Grey - Density, g/cc 1.2 4 ± 0. 0 1 ASTM D 1475 Solid Content 55± 2% ASTM C836/ ASTM C898 Tensile strength 3N/mm² (440PSI) ASTM D 412 Elongation at break > 3 00% ASTM D 412 Full cure@ 25°C 24 hrs. UV resistance @100°C Passes ASTM G154 Service temperature - 5°C to 70°C - Hydrostatic pressure @ 5 bar (50m) No Leakage BS EN 12390 (PART8) Application Temp 5°C to 45°C - Toxicity Non Toxic BS 6920 VOC (g/Ltr) < 20 g/ltr ASTM D3960 SRI Value 100 - 110 ASTM C 1549 - 09 All values are subject to 5 - 10 % tolerance TECHNICAL SPECIFICATION 1 m² / Kg/Coat COVERAGE RATE NEOTEX - SP is available in 20 Kg Pail. PACKAGING Protective clothing such as gloves and goggles should be worn while applying NEOTEX - SP . In case the material splashes to the skin or eyes wash the s ame with fresh water immediately. In critical cases seek medical assistance. HEALTH & SAFETY NEOTEX - SP pails should always be stored in dry and covered areas. The product should not be exposed to direct sunlight or be kept near any source of heat. The product Shelf life is up to 12 months when stored as per the recommended storage conditions. STORAGE & SHELF LIFE NOTE: The information contained in this DATA SHEET, as well as our advice, both written as oral or provided through testing, are based on our experience, and they do not constitute any product guarantee for the installer, who must take them as simple orientations, provided strictly as informatio n. We recommend to study deeply all information provided before proceeding to the use or application of any of our products, and strongly advise to conduct tests “on - site” in order to determine their convenience for a specific project. Our recommendations do not exempt of the obligation that installers have to deeply know the right application method for these systems before they use them, as well as to conduct as many preliminary tests as possible if there are any doubts about the appropriate system to use . The application, use and processing of our products are beyond our control, and therefore under the exclusive responsibility of the installer. In consequence, the installer will be the only responsible of any damage or prejudice derived from the partial or total in - observation of our indications, and in general, of the inappropriate use or application of these materials. Sajaa Industrial Area behind Sharjah Cement Factory, Sharjah U.A.E. Email: info@royalwayindustries.com PO BOX: 65034 Tel: +971 6 572 6378 Website: www.royalwayindustries.com R OYAL WAY INDUSTRIES LLC Page 2

1. TDS - WP - N T01 - 000_ 01/20 PROPRETIES C H AR A C TERISTICS NEOTEX – SP is a single component, high performance acrylic co - polymer based coating, designed to offer excellent long term waterproofing characteristics and resistance to UV degradation, whilst remaining flexible to give excellent crack bridging ab ility.  Single component, easy to apply by brush, roller and spray.  Excellent UV resistance.  Withstands substrate movements.  Provide seamless coating.  Elastomeric, high crack bridging capability.  Environmental friendly, can be applied in confined areas.  Can be applied to a wide range of substrates.  Excellent adhesion to most of the substrates.  Can be applied over existing systems.  Excellent build properties. Enable application to horizontal and vertical surfaces. PROPERTIES NEOTEX - SP Pure Acrylic Protective Coating Page 1 B. Priming On new concrete surface the NEOTEX - SP coating can be applied directly. However, it is highly recommended to apply a priming coat on all old and porous substrates for improving the adhesion of the subsequent coats. The priming coat can be prepared in the work site by diluting NEOTEX - SP with only 10% clean potable water. The priming material shall be mixed thoroughly using a low RPM paddle mixer to ensure proper homogeneity of the mix. Primer application can be done using a brush or roller. For large areas the application can also be do ne using an airless spray machine. The primer should be allowed to dry before applying subsequent coats for at least 6 to 8 hours. The area should be re - primed if there is a delay in the application of the top coat for more than 24hours. C. Top coat Application of NEOTEX - SP is to be done by using a suitable roller or brush. Large areas of application can be done by using an airless spray machine. To achieve an appropriate consistency while using an airless spray we recommend diluting the NEOTEX - SP by a maximum of 10% of potable water. The coating always has to be applied with a minimum of 2 coats for optimum performance. The coverage rate will always vary depending on the area of application and the nature of the substrate. For higher strength an d flexibility, insert a non - woven geotextile membrane whilst the first coat is still wet on all corner joints, fillets and pipe penetration joints. Allow the coating to fully cure for 72 hours to achieve its full properties. NEOTEX - SP is easy to apply, cost effective and particularly used in:  Waterproofing of flashing, roof edgings, walls (either concrete, cement mortar, wood and metal), etc.  Waterproofing of gardens, swimming pools, basement, and sandwich application.  Wet areas, like bathrooms, kitchens, etc.  Protective coating on polyurethane foam insulation. AREAS OF APPLICATION NEOTEX - SP acrylic coating shall be applied as per the following general method of application: A. Substrate preparation: The performance and ultimately the durability of the coating largely depends on the condition of the substrate. Therefore, conditioning and preparation of the substrate is of u tmost importance. Concrete surface: The surfaces shall be thoroughly cleaned to remove all dust particles and laitance. Surface defects like potholes and pinholes on building facades on the concrete shall be repaired with an appropriate polymer modified repair mortar. Metal surface: The surface should be cleaned from all rust scales. This can be achieved by wire brushing or grit blasting. METHOD OF APPLICATION